ENGINEERED FOR EXCELLENCE - NANOKSA G PLUS DISC
Precision and Longevity in Every Nanoksa G Plus Disc
ENGINEERED FOR EXCELLENCE
Precision cuts, unmatched durability, every time.
Nanoksa G Plus Disc is composed of high performance polymers, designed to provide superior cutting performance and long-lasting durability. The disc is made of a special blend of polymers that are designed to resist wear and tear, while providing a smooth, consistent cut. The disc is designed to be used with a variety of dental tools, including drills, grinders, and polishers.
Durable & Long- Lasting
The disc is also designed to be used with a variety of materials, including metal, ceramic, and composite materials. The disc is designed to provide a precise, consistent cut, while reducing vibration and noise. The disc is also designed to be easy to use and maintain, with a long-lasting life.
Effortless Precision:
Just Attach, Cut, and Achieve Flawless
Results with Nanoksa G Plus Disc.
Unmatched Benefits
Durable, precise, and vibration-free for smoother, longer-lasting performance.
Unmatched Strength:
Bacterial Accumulation Prevention :
Aesthetics:
Natural Color
Actual Teeth Weight
Bonding To Surface
Product Detailed Specifications
Material Composition
Strength characteristics :
Absorption (ISO 1047) :
NANOKSA G PLUS has very low water absorption,
which is around 0.1% after 24 hours in water at 23°C.
Solubility (ISO 1047):
NANOKSA G PLUS remains insoluble in common solvents at
room temperature due to its highly crystalline structure.
Tensile Test Maximum Load (ISO 178):
The maximum load in a tensile test for NANOKSA G PLUS
can be in the range of:
Tensile strength at yield: 90-100 MPa
Tensile strength at break: 95-110 MPa
Breaking Load (ISO 178):
Similar to ISO 178, the breaking load for NANOKSA G PLUS
in a tensile test according to ISO 527 is around 95-110 MPa.
Tensile Test Maximum Load
(ISO 178):
Tensile Test Maximum Load
(ISO 527)
The tensile strength values for NANOKSA G PLUS using ISO 527 are generally similar to those obtained using ISO 178:
Tensile strength at yield: 90-100 MPa
Tensile strength at break: 95-110 MPa
Breaking Load
(ISO 527)
Similar to ISO 178, the breaking load for NANOKSA G PLUS in a tensile test according to ISO 527 is around:
95-110 MPa.
Progressive Aesthetics
Detailed specs designed for precision, durability, and same as real
Progressive Aesthetics
Detailed specs designed for precision, durability, and same as real
Progressive Aesthetics
Detailed specs designed for precision, durability, and same as real
Progressive Aesthetics
Detailed specs designed for precision, durability, and same as real
Progressive Aesthetics
Detailed specs designed for precision, durability, and same as real
Ensuring Excellence:
Quality Reports You Can Trust.
Tests of Flexure Strength
Tests of Flexure Strength
Flexure strength tests evaluate a material’s resistance to bending, determining its maximum stress before breaking. This test ensures materials can withstand bending forces, confirming their durability and structural integrity for various applications.
Tests of Flexure Strength
Tests of Flexure Strength